1.中空玻璃生產線粘著磨損，在切向力的作用下，摩擦副表面的吸附膜和服污膜遭到破壞，使表面的輪廓峰在相互作用的各點處發生冷焊，由于相對運動，材料便從一個表面轉移到另一個表面，形成粘著磨損。在此過程中，有時材料也會再次附著回原表面，出現逆轉移，或脫離所粘附的表面而成為游離顆粒。載荷越大，表面溫度越高，粘著的現象也越嚴重。嚴重的粘著磨損會造成運動副咬死。粘著磨損是金屬摩擦副之間普遍的一種磨損形式。

1. Adhesive wear occurs in the production line of insulated glass. Under the action of tangential force, the adsorption film and fouling film on the friction pair surface are damaged, causing cold welding of the surface contour peaks at various points of interaction. Due to relative motion, the material transfers from one surface to another, forming adhesive wear. During this process, sometimes the material may reattach to the original surface, resulting in reverse transfer or detachment from the adhered surface and becoming free particles. The larger the load, the higher the surface temperature, and the more severe the adhesion phenomenon. Severe adhesive wear can cause the motion pair to bite. Adhesive wear is a common form of wear between metal friction pairs.

為了減輕粘著磨損，可采取以下措施：①合理選擇配對材料。同種金屬比異種金屬易于粘著;脆性材料比塑性材料的抗粘著能力強。進行表面處理(如表面熱處理、電鍍、噴涂等)可防止粘著磨損的發生。②限制摩擦表面的溫度。⑤采用含油性和出彩壓添加劑的潤滑劑。④控制壓強。

To reduce adhesive wear, the following measures can be taken: ① Reasonable selection of matching materials. The same metal is easier to adhere to than different metals; Brittle materials have stronger adhesive resistance than plastic materials. Surface treatment (such as surface heat treatment, electroplating, spraying, etc.) can prevent the occurrence of adhesive wear Limit the temperature of the friction surface. ⑤ Using lubricants with oily and extreme pressure additives. ④ Control pressure.

2.中空玻璃生產線磨粒磨損從外部進入摩棕面間的游離硬質顆粒(如塵土或磨損造成的金屬微粒)或硬的輪廓峰尖，在較軟材料表面犁刨出很多溝紋而引起材料脫落的現象，稱為磨粒磨損。磨粒磨損與摩擦副材料的硬度和磨粒的硬度有關。有時選用較便宜的材料，定期更換易磨損的零件，更符合經濟原則。

2. The phenomenon of material detachment caused by abrasive wear on the surface of softer materials, where free hard particles (such as dust or metal particles caused by wear) or hard contour peaks enter between the frosted surfaces from the outside of the insulating glass production line. The abrasive wear is related to the hardness of the friction pair material and the hardness of the abrasive particles. Sometimes choosing cheaper materials and regularly replacing easily worn parts is more in line with economic principles.

3.中空玻璃生產線疲勞磨損，在變接觸應力的作用下，如果該應力超過材料相應的接觸疲勞出眾，就會在摩擦副表面或表面以下一定深度處形成疲勞裂紋，隨著裂紋的擴展及相互連接，金屬微粒便會從零件工作表面上脫落，導致表面出現麻點狀損傷現象.即形成疲勞磨損或稱疲勞點蝕。

3. Fatigue wear of insulating glass production lines. Under the action of variable contact stress, if the stress exceeds the corresponding contact fatigue limit of the material, fatigue cracks will form on the friction pair surface or at a certain depth below the surface. As the cracks expand and connect with each other, metal particles will detach from the working surface of the parts, leading to pitting damage on the surface. This is known as fatigue wear or fatigue pitting.

為了提高零件表面的疲勞壽命，除應合理選擇摩擦副材料外，還應注意：①合理選擇零件接觸面的表面粗糙度。一般情況下表面粗糙度值越小，疲勞壽命越長。②合理選擇潤滑油粘度。粘度低的油易滲入裂紋，加速裂紋擴展。粘度高的潤滑油有利于接觸應力均勻分布，提高抗疲勞磨損的能力。在潤滑油中加入出彩壓添加劑或固體潤滑劑，能提高接觸表面的抗疲勞性能。③合理選擇零件接觸面的硬度。以軸承鋼為例，硬度為62HRc時，抗疲勞磨損能力較高，增加或降低表面硬度，壽命都有較大的降低。

In order to improve the fatigue life of the part surface, in addition to selecting friction pair materials reasonably, attention should also be paid to: ① Reasonably selecting the surface roughness of the part contact surface. In general, the smaller the surface roughness value, the longer the fatigue life Reasonably choose the viscosity of lubricating oil. Oil with low viscosity is prone to penetrate cracks and accelerate crack propagation. Lubricating oil with high viscosity is conducive to uniform distribution of contact stress and improves the ability to resist fatigue wear. Adding extreme pressure additives or solid lubricants to lubricating oil can improve the fatigue resistance of the contact surface Reasonably select the hardness of the contact surface of the parts. Taking bearing steel as an example, when the hardness is 62HRc, the fatigue wear resistance is higher. Increasing or decreasing the surface hardness results in a significant decrease in the service life.

4.中空玻璃生產線腐蝕磨損摩擦過程中，金屬與周圍介質(如空氣中的酸、潤滑油等)發生化學或電化學反應而引起的表面損傷，稱為腐蝕磨損。其中氧化磨損常見，這是金屬摩擦副在氧化性介質中工作時，接觸表面反復生成、磨去氧化膜的磨損現象，實際上是化學氧化和機械磨損兩種作用相繼進行的過程。氧化磨損的大小取決于氧化膜的連接強度和氧化速度。

4. During the corrosion and friction process of insulating glass production lines, surface damage caused by chemical or electrochemical reactions between metals and surrounding media (such as acid and lubricating oil in the air) is called corrosion and wear. Among them, oxidation wear is common, which is a phenomenon of repeated generation and removal of oxide film on the contact surface of metal friction pairs when working in oxidizing media. In fact, it is a process of chemical oxidation and mechanical wear that occur successively. The magnitude of oxidative wear depends on the connection strength and oxidation rate of the oxide film.

本文由中空玻璃生產線友情奉獻.更多有關的知識請點擊:http://www.jncsjx.com真誠的態度.為您提供為多維度的服務.更多有關的知識我們將會陸續向大家奉獻.敬請期待

This article is a friendly contribution from the production line of insulated glass. For more information, please click: http://www.hebeiruizhi.com Sincere attitude. We will provide you with comprehensive services. We will gradually contribute more relevant knowledge to everyone. Stay tuned